非晶纳米晶软磁合金退火工艺研究进展

吕玮1，陈国钧2

（1. 安泰科技股份有限公司，北京 100081；

2. 北京北冶功能材料有限公司，北京 100192）

摘要：非晶纳米晶软磁合金具有绿色节能、成本低廉等诸多优势，已成为战略性新材料领域的研究热点之一。重点概述Fe基非晶纳米晶软磁合金的退火工艺，包括热致晶化、电/磁致晶化、热等静压晶化及薄带连续晶化工艺的新进展。

关键词：非晶纳米晶软磁合金；退火；纳米晶化；磁性能

中图分类号：TG132.2+71 文献标识码：A 文章编号：1001-3830(2015)01-0072-05

Research advance of annealing technology for amorphous

nanocrystalline soft magnetic alloys

LV Wei1, CHEN Guo-jun2

1. Advanced Technology & Materials Co, Ltd, Beijing 100081, China; 2. Beijing Beiye Functional Materials Corporation, Beijing 100192, China

Abstract: Amorphous nanocrystalline alloy has become the hot topic in strategic new materials field as its

advantages of energy saving, low cost, etc. This paper particularly reviews the recent advances of annealing technology for Fe-based amorphous nanocrystalline alloy, including thermal crystallization, electrical/magnetic crystallization, isostatic pressing crystallization, and ribbon continuous annealing.

Key words：amorphous nanocrystalline soft magnetic alloy; annealing; nanocrystallization; magnetic

properties

1 引言?

非晶纳米晶软磁合金[1]具有高起始磁导率（μi）、低矫顽力（Hc）和铁损（Pc）等优异性能[2-4]及绿色环保、成本低廉等特点，已经逐步成为国际战略性新材料领域的研究热点之一[5]，目前已广泛应用于电机定转子材料、高频开关电源及共模电感等器件的商业化生产。具备卓越软磁特性的非晶纳米晶软磁材料可采用非晶合金晶化法制备，因此运用先进的晶化工艺改善合金综合磁性能的研究受到了广泛的重视[6,7]，本文将着重介绍非晶纳米晶合金的热致晶化、电/磁致晶化、等静压晶化及薄带连续晶化工艺的[8,9]研究进展。收稿日期：2014-04-11 修回日期：2014-05-04 通讯作者：吕玮 E-mail: luidavid@126.com

2 热致晶化工艺

2.1 无磁退火(NFA)、横磁退火(TFA)、纵磁(LFA)

退火

非晶纳米晶合金的磁畴在磁场退火中沿外磁退火结束后方向有序的原子对将场方向转动[10,11]，

保持磁场退火期间的取向[12]。图1为不同方式退火后Finemet型Fe基纳米晶合金和Co基非晶态合金的磁滞回线和磁性能对比。可见相比Co基非晶态合金而言，Fe基纳米晶合金Bs值更高，且相对导磁率μ（1kHz）、P0.2/100k等性能在矩形比（Br/Bs）相近的条件下甚至略优于Co基非晶合金。

2.2 旋转磁场退火(RFA)

Herzer等[13]研究了Fe84Nb6B10合金的RFA工艺，并与NFA和TFA作了分析比较，三种工艺的

72 J Magn Mater Devices Vol 46 No1