金属材料拉伸试验试验速率对试验结果的影响

摘要： GB/T228.1-2010《金属材料拉伸试验第1部分：室温试验方法》颁布后，由于标准中对拉伸试验速率提出两种试验速率控制方式：应变速率控制的试验速率（方法A），应力速率控制的试验速率（方法B）。为研究两种试验速率对金属材料拉伸试验结果的影响，做一比对试验，旨在研究试验速率对试验结果数据是否有影响。试验结果表明，两种试验速率控制方式对金属材料拉伸中常规力学性能试验结果影响不大。

关键词：应力速率、应变速率、屈服强度、抗拉强度、断后伸长率、最大力下的总延伸率、平行长度、横梁位移速率

Abstract: the GB/T228.1-2010 “metal materials tensile test part 1: room temperature testing method on after promulgated, because in the standard of tensile test rate proposed two test rate control mode: strain rate control test rate (method A), stress rate control test rate (method B). As the research two test rate on the metal materials tensile test of the outcome, do a comparison test, aims to experiment to test results data rate whether have influence. Test results show that the two test rate control way for metal materials by conventional mechanical test results the impact is not big.

Keywords: stress rate, strain rate, yield strength, tensile strength and elongation at break, the most strongly after total elongation, parallel length, beam displacement rate

1.前言

GB/T228即金属材料拉伸试验方法，该标准是金属材料力学性能最基本、应用最广泛的试验方法。2011年12月1号起，新版标准GB/T228.1-2010《金属材料拉伸试验第1部分：室温试验方法》实施，新版标准同旧版标准（GB/T228-2002《金属材料室温拉伸试验方法》）有较大改动，其中最为显著一点是增加了试验速率的控制方法：方法A应变速率控制方法。方法A是为了减小测定应变速率敏感参数（性能）时的试验速率编号和试验结果的测量不确定度。为了了解方法A应变速率控制方法、方法B应力速率控制方法对力学性能试验结果的影响，特做一比对试验。本试验采用金属材料检测中最为常见的牌号为HRB335，直径14mm热轧带肋钢筋取10根分两组，分别用方法A、方法B进行试验。测定钢筋的屈服强度、抗拉强度、断后伸长率、最大力下的总延伸率，并做数理统计对比计算组间相对偏差，以其判断方法A、方法B对试验结果的影响。