沥青用量对CA砂浆混合料水稳定性影响研究

沥青用量对CA砂浆混合料水稳定性影响研究

沥青用量对CA砂浆混合料水稳定性影响研究

[摘要]：CA砂浆混合料是一种以碎石为主骨架，自制CA砂浆为填充细料的新型路面材料，采用骨架空隙填充法（CAVF法）进行配合比设计，形成骨架密实结构。本文主要研究沥青用量对CA砂浆混合料水稳定性能的影响。试验结果表明：CA砂浆混合料水稳定性较好，油石比为6%时效果最佳。

[关键词]：CA砂浆混合料；水稳定性；浸水马歇尔试验；冻融劈裂试验

[abstract] : CA mortar mixture is a gravel primarily skeleton, homemade CA mortar as the filling material new pavement materials of fine, the skeleton gap filling method (CAVF method) to mix proportion design, form the skeleton close-grained structure. This article mainly studied the asphalt content on the CA mortar mixture water stable performance influence. The test results show that: CA mortar mixture water stability is better, the proportion is 6% for best effect.

[key words] : CA mortar mixture; The water stability; Retain Marshall test; Freeze-thaw splitting test

水泥乳化沥青砂浆(cement asphalt mortar，简称CA砂浆)[1,2]混合料路面材料，采用主骨架空隙填充法（CAVF法）对CA砂浆混合料进行级配设计，以开级配大空隙碎石形成主骨架，CA砂浆为填料形成嵌挤骨架结构。CA砂浆混合料由水泥乳化沥青砂浆和矿料拌制而成，采用冷拌、冷铺的施工工艺，具有适宜的刚度，较高的强度，良好的高温稳定性[3-5]。由于有沥青的加入，在评价其路用性能时，采用沥青混合料的一系列评价方法对该材料的各项性能进行评价。

水稳定性是混合料路用性能之一，也称为抗水损害能力，即抵抗混合料受水的浸蚀逐渐产生沥青膜剥离、掉粒、松散、坑槽而破坏的能力，是影响CA砂浆材料综合性能的重要指标，本文采用浸水马歇尔试验及冻融劈裂试验来对CA砂浆混合料路面材料的水稳定性进行研究及评价。

1 原材料

1水泥:本研究水泥采用P.O32.5普通硅酸盐水泥。

2乳化沥青:本研究采用阳离子慢裂型乳化沥青，其性能如表1所示。

表1 乳化沥青基本性能

试验项目 单位 标准 检测结果